Laser alloying of zinc with aluminum: Solidification behavior

Acta Materialia

Carvalho, PA, Deus, AM, Rui Mário Correia da Silva — 1998 — Elsevier

Informações chave

Autores:

Carvalho, PA, Deus, AM (Augusto Manuel Moura Moita de Deus), Colaco, R, Vilar, R, Patrícia Almeida Carvalho (Patrícia Maria Cristovam Cipriano Almeida de Carvalho), Rogério Anacleto Cordeiro (Rogério Anacleto Cordeiro Colaço), Rui Mário Correia da Silva (Rui Mário Correia da Silva Vilar)

Publicado em

02/03/1998

Resumo

Laser alloyed tracks were produced by blowing aluminum powder into melt pools generated in zinc substrates. Analysis of the microstructures revealed a structural and compositional stratification related with a deficient aluminum redistribution in the liquid. The effect of chemical heterogeneity on solidification mechanisms was modeled. The composition gradients and the solidification undercooling were shown to strongly influence the geometry of the solidification front. A reasonable agreement was obtained between experimental and predicted characteristic dimensions of the microstructures, in particular, the radii of the dendrite tips observed experimentally were comparable to the calculated ones.

Detalhes da publicação

Autores da comunidade :

Versão da publicação

- Versão original do autor

Editora

Elsevier

Ligação para a versão da editora

https://www.sciencedirect.com/science/article/pii/S1359645497002292

Título do contentor da publicação

Acta Materialia

Primeira página ou número de artigo

1792

Última página

1792

Volume

46

Fascículo

5

DOI

10.1016/S1359-6454(97)00229-2

Domínio Científico (FOS)

- Engenharia dos Materiais

Idioma da publicação (código ISO)

- Inglês

Identificador alternativo (URI)

http://www.scopus.com/inward/record.url?eid=2-s2.0-0032472976&partnerID=MN8TOARS

Acesso à publicação:

Acesso apenas a metadados